Full process of forging a classic blacksmith knife out of a roller bearing inner race. This steel is very hard to forge, even very hot. But it does get very hard after quench! As I’ve said at the end I tempered this knife for two cycles of 2hrs at 290°C to hopefully prevent cracks from forming after heavy use.